Pakning af PTFE - FJ 2912D

FJ2912D is made of biaxially-orientated PTFE containing silica. Colour: Pink

  • Standard compressibility
  • Strong acids (except hydrofluoric) to general chemicals
  • Can be used for all concentrations of sulfuric acid
  • Not suitable for molten alkali metals, fluorine gas or hydrogen fluoride
     

FJ2912D is suitable for sealing most chemicals across the whole pH range (0-14) with the exception of molten alkali metals, fluorine gas, hydrogen fluoride or materials which may generate these. FJ2912D is particularly suitable for use in applications involving strong acids.
 

  • Recommended temperature range: -250ºC to 260ºC
  • Recommended pressure range: Vacuum to 85 bar (1230 psi)        
     

Approvals

  • WRAS Approved for use with potable water: Approval No. 1206528
  • TA-LUFT approved
  • BAM Oxygen
  • Tested in accordance to EC Regulation No. 10/2011*
     

*being the specific testing requirements of EN Regulation 1935/2004

 

Typiske applikationer

(Applikation kan ikke oplyses)

Kvalitet (QA) og prækvalifikation

ISO 9001:2008
JQS Achilles (Oil & Gas)
Sellihca (Utillities)

Råmaterialer

Polytetrafluorethylen Biaxially orientated | biaPTFE

Vejr-bestandighed (relativ)
(ikke spec.)
Ozon-bestandighed (relativ)
(ikke spec.)
Olie-bestandighed (relativ)
(ikke spec.)
Vand-bestandighed (relativ)
(ikke spec.)
Damp-bestandighed (relativ)
(ikke spec.)
Syre-bestandighed (relativ)
(ikke spec.)
Base-bestandighed (relativ)
(ikke spec.)
Permeabilitet (relativ)
(ikke spec.)
Brudstyrke (relativ)
(ikke spec.)
Brudforlængelse (relativ)
(ikke spec.)
Sætning (relativ)
(ikke spec.)
Vibrationsdæmpn. (relativ)
(ikke spec.)
Slidstyrke (relativ)
(ikke spec.)
Slagstyrke (relativ)
(ikke spec.)

Accepter cookies

Websitet bruger cookies til at følge din adfærd og for at forbedre brugeroplevelsen.
Du kan altid slette gemte cookies i dine browserinstillinger. Om cookies på sitet ...